| Hi-Flow Comparison Table | |||||||||||||
| HF 105 | HF 225F-AC | HF 225FT | HF 225UT | ||||||||||
| Property | Test Method | Imperial Value | Imperial Value | Imperial Value | Imperial Value | ||||||||
| Color | Visual | Dark Grey | Black | Black | Black | ||||||||
| Reinforcement Carrier | *** | Aluminum | Aluminum | Aluminum | None | ||||||||
| Thickness, (inch) / (mm) | ASTM D374 | 0.0055 / 0.139 | 0.004 / 0.102 | 0.004 / 0.102 | 0.003 / 0.077 | ||||||||
| Carrier Thickness, (inch) / (mm) | ASTM D374 | 0.0015 / 0.038 | 0.0015 / 0.038 | 0.001 / 0.025 | *** | ||||||||
| Elongation, (%45° to Warp & Fill) | ASTM 882A | *** | *** | *** | *** | ||||||||
| Tensile Strength, (psi) / (MPa) | ASTM 882A | *** | *** | *** | *** | ||||||||
| Continuous Use Temp., (°F) / (°C) | *** | 266 / 130 | 248 / 120 | 248 / 120 | 248 / 120 | ||||||||
| Phase Change Temp. (°F) / (°C) | ASTM D3418 | 149 / 65 | 131 / 55 | 131 / 55 | 131 / 55 | ||||||||
| Electrical | |||||||||||||
| Dielectric Breakdown Voltage, (Vac) | ASTM D149 | *** | *** | *** | *** | ||||||||
| Dielectric Constant, (1000 Hz) | ASTM D150 | 3.2 | *** | *** | *** | ||||||||
| Volume Resistivity, (Ohm-meter) | ASTM D257 | *** | *** | *** | *** | ||||||||
| Flame Rating | U.L. 94 | V-O | V-O | V-O | V-O | ||||||||
| Thermal | |||||||||||||
| Thermal Conductivity, (W/m-K) (1) | ASTM D5470 | 0.9 | 1.0 | 0.7 | 0.7 | ||||||||
| Hi-Flow Comparison Table (cont.) | |||||||||||||
| HF 225U | HF 625 | HF 300P1.5 | HF 300G | ||||||||||
| Property | Test Method | Imperial Value | Imperial Value | Imperial Value | Imperial Value | ||||||||
| Color | Visual | Black | Green | Green | Green | ||||||||
| Reinforcement Carrier | *** | None | PEN Film | Polymide | Fiberglass | ||||||||
| Thickness, (inch) / (mm) | ASTM D374 | 0.0015 / 0.038 | 0.005 / 0.127 | 0.0045 / 0.113 | 0.005 / 0.127 | ||||||||
| Carrier Thickness, (inch) / (mm) | ASTM D374 | *** | 0.001 / 0.025 | 0.0015 / 0.038 | *** | ||||||||
| Elongation, (%45° to Warp & Fill) | ASTM 882A | *** | 60 | 40 | 40 | ||||||||
| Tensile Strength, (psi) / (MPa) | ASTM 882A | *** | 30,000 | 7,000 | 400 | ||||||||
| Continuous Use Temp., (°F) / (°C) | *** | 302 / 150 | 302 / 150 | 302 / 150 | 212 / 100 | ||||||||
| Phase Change Temp. (°F) / (°C) | ASTM D3418 | 131 / 55 | 149 / 65 | 131 / 55 | 131 / 55 | ||||||||
| Electrical | |||||||||||||
| Dielectric Breakdown Voltage, (Vac) | ASTM D149 | *** | 4000 | 5000 | 300 | ||||||||
| Dielectric Constant, (1000 Hz) | ASTM D150 | *** | 3.5 | 4.5 | 3.5 | ||||||||
| Volume Resistivity, (Ohm-meter) | ASTM D257 | *** | 10 10 | 10 12 | 10 8 | ||||||||
| Flame Rating | U.L. 94 | V-O | V-O | V-O | V-O | ||||||||
| Thermal | |||||||||||||
| Thermal Conductivity, (W/m-K) (1) | ASTM D5470 | 1.0 | 0.5 | 1.6 | 1.6 | ||||||||